Bộ phận kim loại sinh học - Ningbo Investment Casting Co., Ltd

Bởi Li Chenyu / hcfire360 2021 Tháng Bảy

If you have any demand of Bi-metallic Parts (Bi-metal Parts), please feel free to contact us by email: sales@nbinvestmentcasting.com.
 
Bi-metals are one of our key products. We are able to provide wear-resistant bi-metals with different process:
The 1st type is casting, main material for casting under Wear-resistant White Cast Iron Standard ASTM A532 and High Manganese Steel Standard ASTM A12, main parts as below:


High –Chromium Square Hammer

High-Chromium Flat Hammer

Tấm vuông Ni-Hard

Ni-Hand Ox-Head

Hammer Shank

The 2nd type is the bimetallic composites based on High-chromium cast iron vacuum brazing onto steel backing plate. The welding strength is 320Mpa and the hardness of High-chromium cast iron is 63HRC. The bimetallic composites include many product categories such as chocky bars and blocks, wear buttons, wear bars and blocks and wear plates.


Chocky Bars and Blocks

Mang thanh và khối


Dao kéo cho nhà máy đường

High-Chromium Hammer and Bi-Metallic Hammer Tip

High-Chromium Hammer and Bi-Metallic Hammer Tip


The 3rd type is three layer composites based on tungsten carbide and High-chromium cast iron vacuum brazing onto steel backing plate.


Chocky Bars Welded on Liner

Three Layer Carbide Hammer Tips

High-Chromium Cast Iron and Carbide Welding


The 4th type is strengthen wear parts for Mining and Construction like strengthen blade and teeth based on build-up welding, which mainly include WC flux-cored wire and tungsten carbide particles with strict technical data .


Three Layer Liner

Hàn tích hợp Thanh cacbua bị hỏng

Build-up Welding Strengthen Teeth

Build-up welding bar is completely covered by broken carbide

Build-up Welding Broken Carbide Particles in Different Shaped Objects


The 5th type is strengthen wear parts based on high frequency welding, which high frequency brazing the tungsten carbide on quick wearing position, for agricultural chisel plow sweep, tillage point & Tip and knife blade, etc.


Điểm làm đất nông nghiệp với cacbua vonfram hàn

Breaking Hammer Welded Tungsten Carbide

WC Flux-Cored Wire Build-up Welded strengthen teeth


The 6th type is cast composites compounded by High-chromium and general cast steel to improve wear resistance and assembly. Pour & solidify a wear resistant material to a structural low alloy or carbon steel box.


Snow Shovel Blade

Bi-metallic Box

Hộp kim loại hai mặt cắt phần bên trong


The 7th type is cast composites based on tungsten carbide particles enhancing into High-chromium cast iron to improve wear resistance to a great extent.


Tăng cường các hạt cacbua và thanh gang cao crom

Strengthen Broken Carbide Particles and High-chromium Cast Iron Wear Plates


The 8th type is strengthen surface by plasma transferred arc(PTA) overlay welding. The overlay thickness is 3-30mm, hardness could be controlled range from 60-70HRC. No surface crack, no weld bead and flat surface finish.


10+10mm Thickness Ratios

Strengthen Broken Carbide Particles and High-chromium Cast Iron Wear Plates