Bi-metalik Parçalar - Ningbo Investment Casting Co., Ltd

Li Chenyu / hcfire360 adlı geliştiriciden Temmuz 2021

If you have any demand of Bi-metallic Parts (Bi-metal Parts), please feel free to contact us by email: sales@nbinvestmentcasting.com.
 
Bi-metals are one of our key products. We are able to provide wear-resistant bi-metals with different process:
The 1st type is casting, main material for casting under Wear-resistant White Cast Iron Standard ASTM A532 and High Manganese Steel Standard ASTM A12, main parts as below:


High –Chromium Square Hammer

Yüksek Kromlu Düz Çekiç

Ni-Sert Kare Plakalar

Ni-El Öküz-Kafası

Çekiç Sap

The 2nd type is the bimetallic composites based on High-chromium cast iron vacuum brazing onto steel backing plate. The welding strength is 320Mpa and the hardness of High-chromium cast iron is 63HRC. The bimetallic composites include many product categories such as chocky bars and blocks, wear buttons, wear bars and blocks and wear plates.


Chocky Bars and Blocks

Aşınma Çubukları ve Blokları


Şeker Fabrikası İçin Çatal

Yüksek Kromlu Çekiç ve Bi-Metalik Çekiç Ucu

Yüksek Kromlu Çekiç ve Bi-Metalik Çekiç Ucu


The 3rd type is three layer composites based on tungsten carbide and High-chromium cast iron vacuum brazing onto steel backing plate.


Liner Üzerine Kaynaklı Chocky Barlar

Üç Katmanlı Karbür Çekiç Uçları

Yüksek Kromlu Dökme Demir ve Karbür Kaynak


The 4th type is strengthen wear parts for Mining and Construction like strengthen blade and teeth based on build-up welding, which mainly include WC flux-cored wire and tungsten carbide particles with strict technical data .


Three Layer Liner

Biriktirme Kaynaklı Kırık Karbür Çubuklar

Biriktirme Kaynağı Dişleri Güçlendirir

Build-up welding bar is completely covered by broken carbide

Farklı Şekilli Nesnelerde Kırık Karbür Parçacıklarının Kaynak Oluşumu


The 5th type is strengthen wear parts based on high frequency welding, which high frequency brazing the tungsten carbide on quick wearing position, for agricultural chisel plow sweep, tillage point & Tip and knife blade, etc.


Kaynaklı Tungsten Karbürlü Tarımsal İşleme Noktası

Kırma Çekiç Kaynaklı Tungsten Karbür

WC Özlü Tel Yapısı Kaynaklı dişleri güçlendirir


The 6th type is cast composites compounded by High-chromium and general cast steel to improve wear resistance and assembly. Pour & solidify a wear resistant material to a structural low alloy or carbon steel box.


Kar Küreği Bıçağı

Bi-metallic Box

İç Kesit Kesim Bi-metalik Kutu


The 7th type is cast composites based on tungsten carbide particles enhancing into High-chromium cast iron to improve wear resistance to a great extent.


Karbür Parçacıkları ve Yüksek Kromlu Dökme Demir Çubukları Güçlendirin

Strengthen Broken Carbide Particles and High-chromium Cast Iron Wear Plates


The 8th type is strengthen surface by plasma transferred arc(PTA) overlay welding. The overlay thickness is 3-30mm, hardness could be controlled range from 60-70HRC. No surface crack, no weld bead and flat surface finish.


10+10mm Thickness Ratios

Strengthen Broken Carbide Particles and High-chromium Cast Iron Wear Plates