By Li Chenyu / hcfire360 July 2021

If you have any demand of Bi-metallic Parts (Bi-metal Parts), please feel free to contact us by email: sales@nbinvestmentcasting.com.
Bi-metals are one of our key products. We are able to provide wear-resistant bi-metals with different process:
The 1st type is casting, main material for casting under Wear-resistant White Cast Iron Standard ASTM A532 and High Manganese Steel Standard ASTM A12, main parts as below:

High –Chromium Square Hammer

Жогорку хромдуу жалпак балка

Ni-катуу чарчы плиталар

Ni-Hand Ox-Head

Hammer Shank

The 2nd type is the bimetallic composites based on High-chromium cast iron vacuum brazing onto steel backing plate. The welding strength is 320Mpa and the hardness of High-chromium cast iron is 63HRC. The bimetallic composites include many product categories such as chocky bars and blocks, wear buttons, wear bars and blocks and wear plates.

Chocky Bars and Blocks

Барларды жана блокторду кийиңиз

Кант тегирмени үчүн идиш-аяк

Жогорку хромдуу балка жана би-металлдык балка учу

Жогорку хромдуу балка жана би-металлдык балка учу

The 3rd type is three layer composites based on tungsten carbide and High-chromium cast iron vacuum brazing onto steel backing plate.

Лайнерде ширетилген чоку барлар

Үч катмарлуу карбид балкасынын кеңештери

Жогорку хромдуу чоюнду жана карбидди ширетуу

The 4th type is strengthen wear parts for Mining and Construction like strengthen blade and teeth based on build-up welding, which mainly include WC flux-cored wire and tungsten carbide particles with strict technical data .

Three Layer Liner

Сынган карбид тилкелерин ширетүү

Build-up Welding тиштерин бекемдейт

Build-up welding bar is completely covered by broken carbide

Ар кандай формадагы объекттерде сынган карбид бөлүкчөлөрүн ширетүү

The 5th type is strengthen wear parts based on high frequency welding, which high frequency brazing the tungsten carbide on quick wearing position, for agricultural chisel plow sweep, tillage point & Tip and knife blade, etc.

Ширетилген вольфрам карбиди менен айыл чарба айдоо пункту

Breaking Hammer ширетилген вольфрам карбиди

WC Flux-Coed Wire Build-up Welded тиштерди бекемдейт

The 6th type is cast composites compounded by High-chromium and general cast steel to improve wear resistance and assembly. Pour & solidify a wear resistant material to a structural low alloy or carbon steel box.

Кар күрөгү

Bi-metallic Box

Inner Section Cut Bi-металл куту

The 7th type is cast composites based on tungsten carbide particles enhancing into High-chromium cast iron to improve wear resistance to a great extent.

Карбид бөлүкчөлөрүн жана жогорку хромдуу чоюн куймаларын бекемдеңиз

Strengthen Broken Carbide Particles and High-chromium Cast Iron Wear Plates

The 8th type is strengthen surface by plasma transferred arc(PTA) overlay welding. The overlay thickness is 3-30mm, hardness could be controlled range from 60-70HRC. No surface crack, no weld bead and flat surface finish.

10+10mm Thickness Ratios

Strengthen Broken Carbide Particles and High-chromium Cast Iron Wear Plates